Color: | Gray | Shape: | Powder |
---|---|---|---|
Material: | High Alumina | Refractoriness (Degree): | 1770°< Refractoriness< 2000° |
Application: | Furance | Sample: | Available |
Bulk Density: | 2.4-2.8g/cm3 | Bending Strength: | 7-9Mpa |
Highlight: | high aluminous cement,calcium aluminate cement |
HIGH ALUMINA CEMENT
CA-50/70/80
Detailed Product Description:
Pure calcium aluminate cement is produced by fusing selected raw material in Special furnace. After cooling, the clinker is ground using ball mills.
The raw materials of calcium aluminate cement CA-70 are high purity calcium materials and high pure alumina. The raw materials should be mixed according to suitable ratio. The raw material should be burned to partly fuse. After cooling, α-Al2O3 powder added into clinker, then ground to cement. The content of Al2O3 is usually controlled within 68% to 72%. The principal compounds of it are CA and CA2.
Physical And Chemical Properties
HIGH ALUMINA CEMENT
CA-50
Items | Unit |
A600 |
A700 |
G9 |
||
Chemical composition |
Al2O3 | % | 50-60 | 50-60 | 53.5max | |
CaO | % | 33min | 33.00min | 33.00min | ||
SiO2 | % | 8.00max | 8.00max | 5.50max | ||
Fe2O3 | % | 2.50max | 2.50max | 2.50max | ||
RO2 | % | 0.4max | 0.40max | 0.40max | ||
Specific Surface Aea | cm3/g | 3000max | 3000max | 350min | ||
Beginning Set | min | 60min | 60min | 90min | ||
Ending Set | h | 6max | 6max | 6min | ||
Bending Strength |
1 day | Mpa | 5.50max | 7.00min | 8.00min | |
3 day | Mpa | 6.50max | 8.00min | 10.00min | ||
Compressive Strength |
1 day | Mpa | 40.00max | 50.00min | 72.00min | |
3 day | Mpa | 50.00max | 60.00min | 82.00min | ||
Refractories | ℃ | 1350 | 1350 | 1450 |
CALCIUM ALUMINA CEMENT
Items | Unit | CA-70 |
CA-80 |
||
Chemical composition |
Al2O3 | % | 68.50-72.00 | 78.50-81.00 | |
CaO | % | 28.0-31.50 | 17.00-20.00 | ||
SiO2 | % | ≤0.50 | ≤0.40 | ||
Fe2O3 | % | ≤0.50 | ≤0.30 | ||
K2O+Na2O | % | ≤0.50 | |||
Specific Surface Aea | Cm2/g | ≥5000 | ≥7000 | ||
Beginning Set | min | ≥45 | ≥30 | ||
Ending Set | h | ≤6 | ≤6 | ||
Bending Strength |
24h | Mpa | ≥7.0 | ≥5.50 | |
Compressive Strength |
24h | Mpa | ≥45 | ≥40 | |
Refractories | ℃ | ≥1600 | ≥1790 |
Application :
1. Construction of sulfate corrosion resistance and high temperature proof.
2. Used in rush repairs, leakage stopping , resistance to sulfate attack.
3. Ideal binder for refractoriness such as refractory concrete, refractory castable, ramming mixing, gunning mixing and manmade marble bricks.
4. Ceramic adhesive.
5. Used for sealing coating products and refractory mortar.
6. Used in chemical industry, metallurgical industry,and construction industry.
Features
1. High refractoriness
2. Stable chemical properties, good chemical corrosion performance
3. Ideal plasticity
4. Low shrinking
5. High compression strength, good structural integrity
Package
1 ) . 25KG PP Big Bag In 1MT Big Bag
2 ) . 25KG Paper Bag In 1MT Big Bag
Customized packing availble.
FAQ:
Q : Are you manufacturer or trader?
A : We are manufacturer and have our own factory
Q : Can I get free samples?
A : Yes , We can provide 1 - 10KG for free.
Tel: 86-371-66726695
Fax: 86-371-66726659